Chemical products

Zinc Particle - Repair Colour L232

• High zinc-containing repair colour
• For repairing weld seams and damaged parts at zinced surfaces
• Zinc gleam finish
• Greater than 90% metallic particles in pigment
• Heat-resistant corrosion protection up to +300 °C
• Hardening:
- Dust dry: approx. 15 minutes
- Touch-proof: approx. 45 minutes
- Hardened: approx. 2 - 3 days
Application:
• The substrate must be dry, dust and grease-free
• Apply zinc repair colour in 2 - 3 layers. Allow short flash off time
between coats.

Article No. Article Description
6200 2102 ZC PARTICLE REP.COLOUR 1000ML

Zinc Spray - Bright L244

• For optimum repair, improvement and protection against corrosion of
metallic surfaces
• Active corrosion resistance according to DIN 50021
• Salt spray test at 528 hours according to DIN 20021
• Corrosion resistant zinc coating in hot-dipped colouring
• Weather-resistant and protects against rust and salt
• For aftertreatment of damaged hot-dipped galvanised parts
• Fast drying
• Can be spot-welded
• Overpaintable with commercially available plastic resin paint
systems. Test spraying is recommended.
• Temperature resistant up to +400 °C
• Zinc contents of pigments more than 98 %
• Zinc contents dry film approx. 70 %
• Parts to be treated must be clean, dry, free of grease and rust
• Shake aerosol vigorously for approx. 2 minutes after mixing ball is
heard
• Cross spray from a distance of approx. 20 – 30 cm. One coat usually
sufficient. For additional coats allow 5 minutes between coats.
• Not suitable for over-laying with fillers
• Not suitable as undercoat for PU, MS-polymer and hybrid sealing
compounds

Article No. Article Description
6200 2104 ZINC SPRAY - BRIGHT L244 400ML

Technical data subject to change.
Availability subject to country specific rules and regulations. www.iconridge.com Source: Theo Förch GmbH & Co. KG 813