Page 126 - Catalog 1402-09-12

Cuprium Series Cat6 Cable UTP-SFTP

NC-Cuprum 6UTP
Conductor
Size 23 AWG
Design Type Spacer / Copper Wires / 1 Jacket
0.55 ± 0.5
Diameter (mm)
Insulation
Type UTP
Cable Diameter Nom. 5.5±0.5 mm
Jacket Thickness Nominal Thickness = 0.56 mm
Shielding N/A
Physical
1. Cold Bend Test -30 ± 2°C X 4hrs no crack
2. Dielectric strength AC 1.7KV for 2s
3.Insulation Before Aging | After Aging
Min Tensile Strength (psi) 2400 | 75% before aging (100°C X 48hours)
Min elongation (%) 300 | 75% before aging (100°C X 48hours)
Jacket
Min Bending Radius 50 mm
Installation Temperature -10°C to +60°C
Jacket
Type PVC
Overall Diameter 6.1 ± 0.3 mm
1402-S3
NC-Cuprum 6SFTPI
Conductor
23 AWG
Size
Spacer / Copper Wires / 1 Jacket/Shield/Foil
Design Type
Diameter (mm) 0.5 ± 0.55
Insulation
Type SFTP-Indoor
Cable Diameter Nom. 5.5±0.5 mm
Jacket Thickness Nominal Thickness = 0.56 mm
Aluminium / Polyester Foil
Shielding
Physical
1. Cold Bend Test -30 ± 2°C X 4hrs no crack
2. Dielectric strength AC 1.7KV for 2s
3.Insulation Before Aging | After Aging
Min Tensile Strength (psi) 2400 | 75% before aging (100°C X 48hours)
Min elongation (%) 300 | 75% before aging (100°C X 48hours)
Jacket
Min Bending Radius 50 mm
Installation Temperature -10°C to +60°C
Jacket
Type PVC
Overall Diameter 8.1 ± 0.3 mm

NC-Cuprum 6SFTPO
Conductor
Size 23 AWG
Design Type Spacer / Copper Wires / 1 Jacket/ Shield/Foil
Diameter (mm) 0.5 ± 0.55
Insulation
SFTP Outdoor
Type
Nom. 5.5±0.5 mm
Cable Diameter
Nominal Thickness = 0.59 mm
Jacket Thickness
Aluminium / Polyester Foil
Shielding
Physical
1. Cold Bend Test -30 ± 2°C X 4hrs no crack
2. Dielectric strength AC 1.7KV for 2s
3.Insulation Before Aging | After Aging
Min Tensile Strength (psi) 2400 | 75% before aging (100°C X 48hours)
Min Elongation (%) 300 | 75% before aging (100°C X 48hours)
Jacket
Min Bending Radius 50 mm
Installation Temperature -10°C to +65°C
Jacket
Polyethylene
Type
Overall Diameter 8.3 ± 0.3 mm