Page 13 - PowerPoint Presentation
P. 13
RESIN & ACTIVATOR
FIBERGLASS REPAIR TAPE
• Applicable on dry and wet surfaces.
• Bond with any metal or
• Cures at room temperature (23°C- 25°C).
plastic pipes.
• Easy to mix and apply with 1:1
• Repair leak in 15-30 mixing ratio.
minutes.
• Excellent bonding to all rigid
• Restores pipe to original
substrates.
strength.
• High thixotropy, no shrinkage or
• Resistant to most chemicals
expansion.
(acids, alkalis, salts etc.)
• High adhesion & compressive
• Water activated fiberglass
strength.
wrap
• Withstand pressure up to 400 psi
Viscosity 20,000 - 40,000 cps at 21°C
and temperature up to 200°C.
Specific gravity 1.85
Tensile strength 24,500 psi (1,723
Tensile strength kg/cm2)
36,000 psi (2,531 kg/cm2)
Lap shear strength Compressive strength 35,000 psi
900 psi (63 kg/cm2) (2,461 kg/cm2)
Flexural strength Bond strength 2,900 psi (204 kg/cm2)
26,000 psi (1828 kg/cm2) Flexural strength 42,000 psi (2,953 kg/cm2)
Dielectric strength 16,000 Barcol hardness 40 - 50 Shore D
volts Hardness 85 Shore D
Coverage area (per set)
0.44 m2 @ approx. 1mm thickness Product
Both items Bond to: Steel, • Corrosion protection coating for pipes, storage tanks,
vessels, secondary containment areas, pumps, valves.
Copper, Aluminum, • Uncoated Fiberglass Repair Tape or Carbon Fiber Repair Tape for
composite pipe repair and reinforcement applications.
Galvanised, • Apply with Chopped Strand Mat, Surface Tissue for
Stainless steel, PVC, CPVC, reinforcement, bonding and lamination on surfaces
Fiberglass, Polyethylene,
Polypropylene, FRP pipes
www.australianminingservices.com.au Page 15