FIBER TECHNOLOGY
NUMBER PRODUCT NAME PRICE
TriLor® is a millable fiber-reinforced resin material designed for suprastructures for full arch restorations
and bridge frameworks. This super-strong resin flexes and bends under stress, transferring less energy to
the implants, making it an ideal support material for implant restorations. The TriLor® Arch uniquely allows 3.5mm Arch
the Dental Professional to design the framework using a lathe or handpiece. CAD/CAM TriLor® Pucks are
also available.
50000-35 TriLor® Arch, 3.5mm (3-Pack) 259.95 TriLor
5.5mm Arch
50000-55 TriLor® Arch, 5.5mm (3-Pack) 279.95
50000-75 TriLor® Arch, 7.5mm (3-Pack) 299.95
50000-16 TriLor® 98 CAD Puck, 16mm 249.95 93
7.5mm Arch
50000-20 TriLor® 98 CAD/CAM Puck, 20mm 259.95
50000-25 TriLor® 98 CAD/CAM Puck, 25mm 299.95
50005-16 TriLor® 95 CAD/CAM Puck, 16mm 249.95 Arch Model
50005-20 TriLor® 95 CAD/CAM Puck, 20mm 259.95
50005-25 TriLor® 95 CAD/CAM Puck, 25mm 299.95
TriLor
HIGH PERFORMANCE POLYMER
TRILOR INDICAITONS FOR
SUPRASTRUCTURE DESIGN TriLor
A. Minimum must be 7mm (3.5mm x 2mm)
2
B. Minimum thickness around cylinders is 0.8mm
C. Maximum cantilever is 10mm
TRILOR MATERIAL COMPARISON TriLor 95 Puck
JUVORA Zirconia +
®
Properties TriLor ® Trinia ™ PEKKTON ® CrCo
PEEK Ittrio
Tensile Strength 380 MPa 169 MPa 115 MPa 100 MPa 348 MPa 695 MPa
Flexural Strength 540 MPa 393 MPa 200 MPa 170 MPa 1200 MPa 600 MPa
Tensile Elongation 2% 2.7% 4.4% 20% – 8% TriLor 98 Puck
Flexural Modulus 26 GPa 18.8 GPa 5.0 GPa 4.0 GPa 210 GPa 175 GPa
Compressive Strength 530 MPa 347 MPa 246 MPa 118 MPa 2000 MPa 448 MPa
93