Page 326 - Wurth Total Catalogue

LIQUID METAL FE1

Repair of the motor cover Ideal, fast-acting repair system for installers and workshops
of a small motor in the metal processing field. Especially suitable for filling

shapes, sealing and spackling leaky spots.

• Fe1 is a high-quality two-component reaction resin system that exhibits
characteristics of metal due to its special formula.
• The ideal mixing ratio of the components (A:B = 1:1, pressing out two
strands of the same length from the tubes) makes faulty mixing of the
repair mass almost impossible.
• Fe1 is specially designed for smaller repair jobs under pressure of time.
• Fe1 can be applied with a spatula and does not run, which makes
Bearing point, repaired vertical application possible as well.
and then reworked. • After hardening, Liquid Metal Fe1 can easily be processed via lathing,
milling, drilling, filing or thread cutting, just like with metal.

Description Contents Art. No. Pack Qty.
Liquid Metal FE1 500 g 0893 449 1

Glass Fabric Ribbon:
• For strengthening the metal mass when repairing with Liquid Metal Fe1.
• Dimensions: 1,000 x 50 x 1.3

Technical Data Description Contents Art. No. Pack Qty.

Mixture Ratio component A : component B = 1:1 Glass Fabric Ribbon - 0894 650 1
Tack Cure Time 7–12 min. (at room temperature)
Hardening Time 4–24 h (at room temperature) Processing Instructions:
Pot Life 5 min./20 g (at room temperature) The metals must be cleaned and degreased bare. Mix components A and
Consistency does not run B homogeneously 1:1. Apply mixture immediately with a spatula (short pot
Spec. Weight 2.80 (components A and B mixed) life). The hardened liquid metal can be lathed, milled, drilled etc. Please
Compressive Strength 70 N/mm 2 note the accompanying application instructions.
Tensile Strength 12.5 N/mm 2
Shear Tension 14.5 N/mm 2 Applied thickness: 0.5-10mm
Temperature Resistance 0.7 kcal/mh °C, – 60°C to + 120°C Maximum thickness: 20mm
Dimensional Stability/Martens + 40 °C Layers can be repeated once fully cured.
Linear Expansion Coefficient + 40 x 10 1 °C
–6

Application Overview
Abrasions on: Leak-sealing on: Blowholes in: Run-in damage on: Creation of:
• Pump Housings • Cooling units • Grey cast iron during casting • Shafts • Shapes
• Impellers • Tanks • Grey cast iron during processing • Hydraulic cylinders • Retainers
• Propellers • Water Tanks • Blocks • Models
• Rudders • Water Pipes • Bearing seats • Guides
• Heat Exchangers • Oil Pipes • Crankcases • Prototypes
• Condensers
• Housings
AUS. pub. 08/10 © • Dust Pipes
• Slides
• Chutes
• Bolts
• Torn-out Threads