FAST-ACTING EPOXY RESIN ADHESIVE ESK-50 Solvent-free two-component adhesive

suitable for bonding together various
materials with high tensile and high
impact strength and excellent resistance
to flaking and shocks.

Fast curing.
The reaction of the two components results in a
A
fast binding speed, ensuring fast application.

High tensile strength values.
Tensile shear strengths are maintained even under
the in uence of heat.

Outstanding resistance to chemicals.
Resistant to many liquids such as petrol, many
lubricant oils and water.
B
Can be sanded when fully cured.

Resistant to aging.

Art. No. 0893 480 1* High transparency.
Contents 50 ml
Chemical basis Epoxy resin Silicone-free and solvent-free.
Colour Transparent
Min. processing time 4 min Application area.
Min. combined tension and shear strength resistance 20N mm 2 For adhering stainless steel sheets to each
Min. final strength 2 h other, repairing shorn plastic and metal parts,
Min./max. temperature resistance -60 to 100 C manufacturing PCBs etc.
Shelf life from production 36 Month
Bondable materials:
ncludes 2 Mi ing Tubes
Steel, galvanised steel, stainless steel, aluminium,
For use with Image Description Art. No. Quantity copper, brass, sanded glass fibre-reinforced
Art. No. 0893 480 1 A Static mixing tube 0891 481 1 plastic, ABS, hard PVC, SMC, glass, ceramic,
concrete, wood and polyurethane.
Partner Products: Notice:
Image Description Art. No. Instructions: For safety reasons (due to cartridge filling
B Double Cartridge Gun 0891 893 485 • The static mixing tube is attached to the technology) the first 20 g of mi ed adhesive
double cartridge of the S -50 and the should not be used for bonding. Uncured
Hardening speed for tensile shear cartridge is inserted into the gun. adhesive can be removed using acetone.
strengths of >10 N/mm2: • The adhesion must be evenly pressed until
Temperature hardening time final strength is achieved.
10 C appro . 120 min. • The best adhesive bonding strengths are
achieved after cleaning and sanding with a
15 C approx. 70 min. maximum bonding gap of 0.1 mm.
23 C approx. 60 min. • The curing time is dependent on the
40 C appro . 25 min. temperature.
60 C approx. 10 min. • If work is interrupted for longer than
3 minutes, change the positive mixer.
100 C appro . 2 min.